Products
  • 1. Titanium Dioxide –BLA001(for paper making)
  • It is white powder, yellow when heated. Insoluble in water, organic acid and weak inorganic acid, soluble in basic a little. It has high refractory rate good whiteness, strong masking power and dispersity. Otherwise, it has good chemical trust resisting property, heart endurance and violet ray bloom resisting property.
    1) Use: Mainly used in paper making, aquosity coating, chemical fibre and so on.
    2) Packing: In 25kg woven bag with inner film.
    3) Specification:
  • Items
  • Results
  • Purity(TiO2),% ≥
  • 98.0
  • Whiteness(compared with standard sample) ,% ≥
  • 95.0
  • Tinctorial power(compared with standard sample)% ≥
  • 96.0
  • Oil absorption, g/100g ≤
  • Up to customer
  • Water absorption,g/100g ≤
  • 28
  • PH (water dispersed solution)
  • 6.5-8.5
  • Reside on sieve of 45mm,% ≤
  • 0.05
  • Volatile constituents at 105 °C,% ≤
  • 0.5
  • Water dispersity ,% ≥
  • 75
  • Power brightness L,% ≥
  • 98.0
  • Power whiteness WG,% ≥
  • Up to customer
  • Masking power , g/m2
  • Up to customer
  • 2. Super Durability Universal Rutile TiO2-BLR601
  • Super Durability Universal Rutile TiO2-BLR601 is a kind of universal rutile titanium dioxide which is coated with Titanium, silica, aluminum etc, after extra-fined treatment, and with special organic surface treatment. It has a super durability and high opacity. It is widely used in the area of plastic, rubber, paper and high grade pigment, especially used in the macromolecule system, such as plastic steels, color master batch and powder pigment and also in solvent based coating, printing ink which under the outdoor super durability environment.
    1) Standard adoption:
    ISO591:2000(E): R , ASTM D47600: V
    2) Packing: In 25kg or 1000kg woven bag with inner film.
    3) Specification:
  • Item
  • First Grade
  • Standard
  • TiO2 content %≥
  • 93
  • 93
  • Color(compared with standard sample)
  • No inferior to
  • Slight different with
  • Tinctorial power(compared with standard sample)≥
  • 105
  • 100
  • Volatile constituents at 105 °C %≤
  • 0.6
  • 0.8
  • Resistivity of water liquid extract Ωm≥
  • 60
  • 50
  • Oil absorption (g/100g)≤
  • 21
  • 24
  • Residue on sieve of 45 µm(m/m) %≤
  • 0.05
  • 0.1
  • Rutile crystal content %≥
  • 97
  • 95
  • PH of Aqueous suspension
  • 6.5-8.0
  • 6.0-8.5
  • 3. Titanium Dioxide Anatase BA01-01
  • It can be used in paint, rubber, plastic, paper making, printing ink, chemical fiber industry, etc.
    1) Packing: In 25kg or 1000kg woven bag with inner film.
    2) Specification:
  • Item
  • Superior grade
  • First grade
  • Standard
  • TiO2(m/m), % ≥
  • 98.0
  • 98.0
  • 98.0
  • Color(compared with standard sample)
  • Approximate
  • No inferior to
  • little inferior to
  • Tinctorial power(compared with standard sample)≥
  • 100
  • 100
  • 90
  • Volatile constituents at 105 °C %≤
  • 0.5
  • 0.8
  • 1.0
  • 105 °C Volatile after 24hr pre-treatment ≤
  • 0.5
  • 0.5
  • 0.5
  • Soluble in water(m/m) %≤
  • 0.4
  • 0.5
  • 0.6
  • PH value
  • 6.5-8.0
  • 6.5-8.0
  • 6.5-8.5
  • Oil absorption (g/100g)≤
  • 22
  • 26
  • 28
  • Residue on sieve of 45µm (m/m) %≤
  • 0.05
  • 0.10
  • 0.30
  • Resistivity of water liquid extract Ωm≥
  • 30
  • 20
  • 16
  • Sodium PerborateSodium PerborateSodium Perborate
  • § Note: Pictures above are the reference. The criterion is the object.
Back
Main products: Thiourea Dioxide | Sodium Percarbonate | FAS | Furfuryl Alcohol | Furfural | Thiourea | Melamine | TAED | Titanium Dioxide | 2-Ethyl Anthraquinone